UV Transfer Coating Fireproof Insulation Board , Decorative Insulated Wall Board

UV Transfer Coating Fireproof Insulation Board , Decorative Insulated Wall Board

 

Specifications:

 

Product Performance
UV coating Decorative Insulation

Board

Decoration

Layer

UV coating decorative board Water-resistant, fire-resistant, anti-pollution, anti-scratch, anti-abrasion, anti-acid , alkali resistance, impact resistance,UV-Resistance and weather resistance Precious stone pattern, color, and gloss optional designed; Same using life for indoor use and building, the outdoor life is more than 25 years.
Insulation Layer EPS insulation layer

(Grade B1)

Heat conductivity ≤0.041. volume-weight :18kg / m³ with the tensile strength:110–120kpa; volume-weight 20kg / m³ with the tensile strength :140kpa.
XPS insulation Layer

(Grade B1)

Heat conductivity ≤0.030. Volume-weight 25–45kg / m³ & tensile ≥150kpa. Strong compressive resistance. 30-40 years average using life. Excenllent structure load-bearing performance .
Polyurethane insulation board

(Grade B1)

Hard polyurethane with low thermal conductivity, good thermal performance. When the hard polyurethane with the density of 35 ~ 40kg / m3, thermal conductivity is only 0.018 ~ 0.024w / (m.k), equivalent to half of the EPS, is the lowest heat conductivity of all the insulation materials .
TPS insulation board

(Grade B1)

Heat insulation thermal conductivity is 0.060W / (m · k) ,it has good tensile compressive strength , impact resistance and stability ; its compressive strength reaches 150-500KPa
Rock wool (Grade A) Appearance quality: smooth surface, without prejudice practical scars, stains damaged. Combustion performance: non-combustible. Thermal load contraction temperature: 643 degrees.
Moisture absorption: 3.9%. Organic content: 2.9%.
Rockwool board basic parameters:
Material: rockwool
Apparent density: Rockwool 120 (kg / m3)
Heat conductivity: 0.04 (W / (m.K))
Max operating temperature: 80 (℃)
Specifications: 950,1150 (mm )
Operation standard: GB
Operating temperature: 80 (℃)
Phenolic Foam Board(Grade B Grade A) Not be melt at high temperatures ,not be softened, with low smoke, non-proliferation flame resistance, flame penetration, There is no distortion, no burning ,no fire, being placed 10 minutes at 1400 ℃, can effectively prevent the flames and smoke spread

 

Weidi Decorative Insulation Board system performance index

 

Item Detection standard and requirements The third party test
results
Weather resistance JF149-2003,
JGG144-2004
After weather resistance test,
No damage such as facing layer
blistering or falling off,Protective
layer hollowing or falling off; No
seepage crack appear.
No damage such as
facing layer blistering
or falling off,Protective
layer hollowing or
falling off; No seepage
crack
JG149-2003,
JGJ144-2004
Impact-resistance strength
grade:10
Water absorption
g/㎡,Immersed
24H
JG149-2003,
JGJ144-2004
≤500 21
Wind pressure
resistance value
KPa
JG149-2003,
JGJ144-2004
Not less than the wind load
design value of the project
After 15 kpa level wind
load esistance test,,no
water seepage
Freezing and
thawing resistance
JG149-2003,
JGJ144-2004
No surface cracking,hollowing,
blistering,exfoliation
No surface cracking,
hollowing,blistering,
exfoliation
Steam flow density

g/(㎡·H)

JG149-2003,
JGJ144-2004
≥0.85 2.36
Watertightness JG149-2003,
JGJ144-2004
Sample protective layer inside
without water infiltration
Sample protective layer
insidewithout water
infiltration
Thermal conductivity

W/(m·k)

GB/T10801.1-2002,
JG149-2003
≤0.041 0.033
Apparent density
kg/m³
GB/T10801.1-2002,
JG149-2003
18.0-22.0 19
The compressive
strength perpendicular
to the panel MPa
GB/T10801.1-2002,
JG149-2003
≥0.10 0.10
Dimensional
stability %
GB/T10801.1-2002,
JG149-2003
≤0.30 Length Change 0.13
Width Change 0.15
Thickness Change 0.24
Compression
strength KPa
GB/T10801.1-2002,
JG149-2003
≥60 99
Water vapor
permeability
ng/(Pa·㎡·s)
GB/T10801.1-2002,
JG149-2003
≤60 4
Water absorption
(Volume fraction)%
GB/T10801.1-2002,
JG149-2003
≤6 2
Tensile bond strength

MPa
(Connected with
cement mortar)

Original intensity JG149-2003 ≥0.60 0.94
Water resistant JG149-2003 ≥0.40 0.54
Tensile bond strength

MPa
(Connected with

Expanded
polyphenyl board)

Original intensity JG149-2003 ≥0.10,Destroy interface on
EPS Board
≥0.10,Destroy interface
on EPS Board
Water resistant JG149-2003 ≥0.10,Destroy interface on
EPS Board
≥0.10,Destroy interface
on EPS Board
Operational time
H
JG149-2003 1.5-4.0 4.0
Single anchor bolt
tensile standard
capacity KN
JG149-2003 ≥0.30 0.83

 

Weidi Decorative Insulation Board overall dimension specification

 

Test Item Detection standard and requirements The third party test results
Dimensional Deviation Length(mm) GB/T7748-1999 ±1.5 -1.0~0
Width(mm) ±1.5 -1.0~0.5
Thickness(mm) ±0.5 -0.2~0.1
Diagonal difference(mm) ≤2.0 0.5
No straight degree in Border(mm/) ≤2.0 0
Warping degree(mm/m) ≤3.0 0

 

Weidi Decorative Insulation Board final product facing layer performance

(varieties: solid color/metal/stone/wood grain/special effects, etc.)

 

Test Item Detection standard

and requirements

The third party test results
Coating thickness(μm) GB/T13452.2-

2008-10

≥30 199
Coating adhesion(MPa) GB/T5210-2006 ≥0.3 1.7(0.8-2.7),100%A
Hardness(Pencil) GB/T6739-2006 ≥4H 6H No scraping damage
Abrasive resistance(750g/500r)

,Suitable grinding wheel type:CS-10

GB/T1768-2006 0.003
Solvent resistance wiping(Butanone,

100times)

HC/T-3792-2005

Appendix

No undercasing Meet the requirement
Acid-resistance(5%HC1 liquor,24H) GB/T9274-1998 No blistering,No Falling off,non-discolouring No Change
Alkali resistance GB/T9274-1998 No blistering,No Falling off,non-discolouring No Change
Abrasion performance HC/T3793-2005-

4.1/4.3

≥5 12
Stain resistance GB/T9757-2001

Appendix A

≤5 5
Scrub resistance GB/T9266-2009 ≥10000 >10000
Oil resistant(Immerse in engine oil SE15W-40 24H) GB/T9274-198888 No blistering,No Falling off,non-discolouring No Change
Alkali burnout resistance(72H) JG/T210-2007 No abnormalities
Salting-out resistance(144H) JG/T210-2007 No abnormalities
Weather resistance GB/T1865-2009,GB/T1766-2008 Artificial climate ageing and radiation exposure 4000Hrs after testing,Dulling≤3Grade,

Discoloration≤2Grade

 

Description:

 

Decoration Veneer Layer: UV Coating

Carrying Layer: Calcium silicate board;Cement pressure plate;Aluminium plate;Galvanized aluminium plate

Insulation Layer: Polyurethane plate;TPS plate;XPS plate;EPS plate;Rock wood plate;Phenolic aldehyde Plate

 

UV coating board is a a new type of inorganic fire dalle high simulation baord used the special fiber reinforced cement as base material, surface is repeatedly polished, permeated, waterproof , after roller coating and spray coating layer the fluorocarbon paint, then printing the prepaired natural stone colour and pattern UV fluorocarbon film on the based board by the thermal transfer process,after that again roller coating and spray coating layer the fluorocarbon paint , finally 13 times uv-curable process.

 

Applications:

 

Business Organizations It is widely used in office building,hotel, High-end residential and other building’s decoration and insulation project.